Very High Cycle Fatigue Properties of Carburized Steel by Ultrasonic Torsional Fatigue Testing

DOI Web Site 2 Citations 3 References

Bibliographic Information

Other Title
  • 超音波ねじり疲労試験機による浸炭鋼の超高サイクル疲労特性の解明
  • チョウオンパネジリ ヒロウ シケンキ ニ ヨル シンタン コウ ノ チョウコウサイクル ヒロウ トクセイ ノ カイメイ

Search this article

Abstract

In this study, an ultrasonic torsional fatigue testing machine was developed in order to investigate the very high cycle fatigue properties of carburized steels. The testing machine can apply more than 800MPa of shear stress amplitude at 18.3kHz. The very high cycle fatigue diagram and crack propagation behavior of carburized SCM420H were obtained by using the testing machine and compared with results of non-carburized SCM420H. Fatigue crack initiation and growth was observed in very high cycle regime for both carburized and non-carburized SCM420H. It was found that carburizing of SCM420H was effective to enhance the fatigue life in very high cycle regime. In addition, crack deflection from mode II to mode I under torsional fatigue was discussed based on the fracture mechanics.

Journal

Citations (2)*help

See more

References(3)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top