- The Effect of Heat Treatment on the Mechanical Properties of 17-7PH Stainless Steel
- 17-7PH ステンレス コウ ノ キカイテキ セイシツ ニ オヨボス ネツ ショリ ノ エイキョウ
この論文をさがす
説明
The effect of heat treatment on the mechanical properties of 17-7PH (17% Cr, 7% Ni, 1% Al) stainless steel was investigated at room temperature. The specimens were given the following heat treatment conditions: (a) Solution treatment: 1050°C×15min, a.c. (b) Intermediate treatment: 760°C∼975°C×15min, a.c. (c) Subzero treatment: -78°C×8hr. (d) Aging treatment: 425°C∼575°C, 0∼70hr, a.c. The results obtained can be summarized as follows:<br>(1) Austenite in the solution treatment could be transformed into martensite by intermediate and subzero treatments, so that tensile strength, yield strength, plane-bending fatigue limit and hardness increased, but elongation considerably decreased.<br>(2) After subzero treatment, the mechanical properties of this steel increased a little with increasing intermediate temperature.<br>(3) In the relation between aging conditions and hardness, the lower the aging temperature, the longer was the aging time that showed a maximum value of hardness, but its value rose high.<br>(4) When the aging conditions continued within the temperature range of 425°C to 575°C for 2 hours, the maximum mechanical properties could be obtained at 500°C. In this case, there was hardly the effect of intermediate temperature except elongation.<br>(5) When the specimens intermediate-treated at 950°C were aged at 500°C, these tensile strength, yield strength, fatigue limit and hardness were remarkably increased in the early stage of aging and showed the maximum values in 2 hours. But these elongation was nearly constant up to 7 hours.<br>(6) In the condition of subzero treatment or aging treatment the ratio of the fatigue limit to the tensile strength was about one-third.
収録刊行物
-
- 材料
-
材料 17 (176), 415-419, 1968
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680395639936
-
- NII論文ID
- 110002294486
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 8219541
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可