- High Temperature Strength of Structure-Controlled Ni-Al-Mo In-Situ Composites
- ソシキ セイギョ シタ Ni Al Moケイ In Situ フクゴウ ザイリョウ ノ コウオン キョウド ヒョウカ
この論文をさがす
説明
The microstructural-controlling of uni-directionally solidified Ni-Al-Mo in-situ composites has been conducted by changing growth rates and by the addition of rhenium (Re) or iridium (Ir). Oxidation resistance at 1000°C in air and high temperature strength at 800°C of these in-situ composites have also been examined and have been compared with those of conventional Ni-base superalloys, such as MAR-M247 and IN-100. The morphology of strengthening phase, that is Mo phase, changed from fiber-like shape to plate-like shape with increasing the growth rate. A superior oxidation resistance evaluated for 30h was observed for Ni-Al-Mo-Ir in-situ composites. On the other hand, high strength and large fracture strain were obtained for Ni-Al-Mo-Re in-situ composites. Experimental results showed that these composites possessed excellent high temperature properties, which was better than or comparable with those of Ni-base superalloys.
収録刊行物
-
- 材料
-
材料 52 (7), 838-842, 2003
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680396143360
-
- NII論文ID
- 110002302179
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 6647948
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可