高濃度のアルカリを含む混合アルカリほう酸塩ガラスの密度

DOI Web Site

書誌事項

タイトル別名
  • Density of Mixed-Alkali Borate Glasses with High-Alkali Content
  • コウ ノウド ノ アルカリ オ フクム コンゴウ アルカリ ホウサンエン ガラ

この論文をさがす

説明

The glass forming regions in the mixed-alkali borate systems with high-alkali contents were determined. The densities of the resultant glasses at room temperature were measured by the buoyancy method, from which the apparent molar volumes were calculated. The relationships between these properties and compositions of glasses were investigated.<br>The main results obtained were:<br>(1) The effectiveness of alkali ions for the glass formation in the single- and mixed-alkali borate systems is in the order of Li>Na>K.<br>(2) The apparent molar volume-composition curve is nearly linear for the Li-K glasses. On the other hand, the curve has a negative deviation from linearity for the Li-Na glasses and a positive one for the Na-K glasses. The experimental results were discussed in terms of the theory of field strength.

収録刊行物

  • 材料

    材料 25 (275), 765-770, 1976

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ