- Consideration on Behavior of Fatigue Crack Propagation by Dislocation Dynamics Simulation
- テンイ ドウリキガク シミュレーション ニ ヨル ヒロウ キレツ シンテン キョドウ ノ ケントウ
この論文をさがす
説明
The influence of the loading history and stress ratio on the behavior of fatigue crack propagation was investigated through the computer simulation based upon the emission and movement of dislocations from the crack-tip. The result of the simulation showed that there is a power relation between the stress intensity range in the preceding cycles and the threshold value where the crack stops propagating. It was also found that the threshold value obtained by the simulation is closely connected with the stress ratio through the Walker relation. The existence of those relations was explained from the viewpoint that the above two parameters control not only the maximum stress intensity but also the crack opening stress intensity level which is determined by the degree of the shielding effect due to the residual dislocations. This idea was supported by the simulation result that the crack propagation rate was clearly related to the effective stress intensity range which was defined as the difference between the maximum stress intensity and the above crack opening stress intensity.
収録刊行物
-
- 材料
-
材料 52 (11), 1285-1291, 2003
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680396515840
-
- NII論文ID
- 110002302032
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 6769217
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可