- A Study on ODA Formation Condition for High Strenght Steel during Fatigue Test in Vacuum
- シンクウ ヒロウ シケン ニ ヨル コウキョウド コウ ノ ODA ケイセイ ジョウケン ノ ケントウ
この論文をさがす
説明
A high strength steel shows fish-eye failure in very long life fatigue. In this region, the fatigue crack growth in ODA (Optically Dark Area) controls the fatigue process. However, ODA's formative mechanism is unknown. Therefore, to predict fatigue life of fish-eye failure, it is important to know ODA's formative mechanism. So, the present study examined for the influential factors on ODA in the fatigue process through uniaxial push-pull fatigue tests in vacuum as well as computer simulation. In experiment, vacuum environment is employed to simulate fish-eye type crack growth on surface of specimens becase of shutting off supply of air. The test results in vaccum showed that the fatigue life property of surface failure has corresponded to fish-eye fatigue life. And the site of inclusion which has fracture origin size determines whether surface failure or internal failure in vacuum. The results of fractographic observation of crack initiation showed that the rough area of surface fracture in vacuum was formed by mechanism of ODA type crack. Furthermore, the fatigue life of numerical simulation in vacuum showed that the fatigue life which was necessary to form ODA on specimen surface corresponded experimental life.
収録刊行物
-
- 材料
-
材料 54 (12), 1213-1216, 2005
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680396583168
-
- NII論文ID
- 110006266438
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BD28Xjs1amsw%3D%3D
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 7768599
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可