書誌事項
- タイトル別名
-
- Corrosivity Test of Industrial Waters
- コウギョウ ヨウスイ ノ フショクセイ シケン
この論文をさがす
抄録
The applicability of the method of estimating corrosion rates from cell voltage-current curves was investigated as a rapid method to evaluate the corrosivity of industrial waters.<br>Cell voltage-current curves and weight losses of mild steel were measured in 30g/l sodium chloride solution containing 6.9ppm dissolved oxygen gas at 26±1°C.<br>It was found that the corrosion rates measured by this method were in good agreement with those found by weight loss measurement, if the sweep velocity of cell voltage was less than 100mV/min and the area ratio of anode to cathode was more than 1.<br>Then, corrosion rates of mild steel in the industrial waters at Kawasaki city were measured, and it was indicated that the corrosion rates measured by this method were slightly larger than those found by weight loss measurement.
収録刊行物
-
- CORROSION ENGINEERING DIGEST
-
CORROSION ENGINEERING DIGEST 14 (4), 159-162, 1965
社団法人 腐食防食協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680406790912
-
- NII論文ID
- 130004981250
- 130006141148
-
- NII書誌ID
- AN00261781
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 8446024
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可