大型特殊鋼材の軟化焼鈍への等温變態の應用(I)

DOI Web Site

書誌事項

タイトル別名
  • FULL ANNEALING OF LOW ALLOY STEEL THICK FORGINGS BY A ISOTHERMAL TRANSFORMATION. (I)

この論文をさがす

説明

The purpose of this study was to save fuels, equipments and labours reguired for full annealing of low alloy steel thick forgings.<BR>In this first report, theory of isothermal annealing and fundamental studies carried out on small spacimens were given.<BR>The steel used was a medium C low Ni-Cr-Cu-Mo steel contg. 0.30-0.35% C, 0.6-1.0% Mn, 1.0-1.8% Ni, 1.0-1.3% Cr, 0.2-0.4% Cu and 0.4% Mo.<BR>To determine the S-curve of this steel, thermal expansion was measured aud microstrueture and hardness of specimens quenched after isothermal heating were investigated.<BR>The results obtained were summarized as follows:<BR>(1) This steel can be full annealed whithin 5 hrs. if its supercooled austenitic state is kept and transformed at 660-670°C, 6 hrs. at 650-680°C and 9 hrs. at 640°C<BR>(2) The isothermally annealed steel is satisfactorily softened and its Brinnel hardness number is below 200.<BR>(3) The microstructure of the isothermally annealed steel is quite different from that of the ordinary annealing, but the time required for heating in the quenching operation those steels was not varied between these two different annealing structures.<BR>(4) That different annealing process has no influence on the mechanical properties of the steel after hardening and tempering.

収録刊行物

  • Tetsu-to-Hagane

    Tetsu-to-Hagane 35 (10), 355-359, 1949

    一般社団法人 日本鉄鋼協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ