The Relationship between Hillock Formation Temperature and Initial Residual Stress in Copper Thin Films with Different Crystal Grain Size

DOI Web Site 1 Citations 5 References

Bibliographic Information

Other Title
  • 結晶粒径の異なる銅薄膜のヒロック形成温度と初期残留応力の関係
  • ケッショウ リュウケイ ノ コトナル ドウ ハクマク ノ ヒロック ケイセイ オンド ト ショキ ザンリュウ オウリョク ノ カンケイ

Search this article

Description

We deposited copper films which have a different grain size on the silicon single crystal wafer with dc magnetron sputtering. The crystal grain size of the copper films was varied by changing the substrate temperature Ts, which is one of the sputtering deposition conditions, between 64°C and 200°C. The obtained copper films were set on an optical microscope equipped with a vacuum heating device. The films surface were observed with the microscope throughout the thermal cycling between room temperature to 800°C. Next, we examined the temperature which hillocks begin to form. As a result, we confirmed the clear relationship between the temperature which the hillocks begin to form and the initial grain size of the copper film. In the case of low substrate temperature of Ts = 64°C, the initial grain size of copper film was very small, and many hillocks were formed at low heating temperature of 300°C. On the other hand, in the case of high substrate temperature of Ts = 200°C, the initial grain size of copper film was large, and hillocks were not formed below heating temperature of 800°C.

Journal

Citations (1)*help

See more

References(5)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top