- Effect of Shot Peening with Fine Zirconia Shot on Fatigue Property of Friction Stir Welded A6061 Alloy
- A6061 ゴウキン FSW ツギテザイ ノ ヒロウ トクセイ ニ オヨボス ジルコニアピーニング ノ エイキョウ
この論文をさがす
抄録
Fatigue tests of friction stir welded (FSWed) joints of A6061-T6 aluminum alloy have been conducted with fully reversed plane bending conditions (R= -1) to investigate the effect of shot peening on the high cycle fatigue property. Shot peening was performed with two types of fine zirconia shot grid. The results showed that the fatigue strength at 107 cycles of unwelded specimens (base material) was 130 MPa and fine zirconia shot peening enhanced the strength by 10 MPa with B120 shot grid type. The fatigue lives were dramatically improved in all stress levels by the peening. On the other hand, the fatigue strength at 107 cycles of the SP treated FSWed specimens was nearly the same as that of the base material, and the fatigue lives were improved at only lower stress levels. To discuss these fatigue properties, fracture surfaces were observed and peening effects such as surface roughness, hardness and residual stress distributions were examined.
収録刊行物
-
- 材料
-
材料 63 (8), 596-601, 2014
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680421537920
-
- NII論文ID
- 130004678633
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 025759416
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可