- Strength and Temperature Increase of <i>β</i>-Ti Alloy during Quasi-Static and Impact Compressive Deformation
- 準静的および衝撃圧縮変形時のβ型チタン合金の強度と温度上昇
- ジュンセイテキ オヨビ ショウゲキ アッシュク ヘンケイジ ノ vガタ チタン ゴウキン ノ キョウド ト オンド ジョウショウ
- Strength and Temperature Increase of ^|^#946;-Ti Alloy during Quasi-Static and Impact Compressive Deformation
- Strength and temperature increase of β-Ti alloy during quasi-static and impact compressive deformation
この論文をさがす
抄録
Titanium alloy is one of the typical aerospace structural materials because of its lightness, high specific strength, and high corrosion resistance. However, it has extremely low thermal conductivity, too. This causes relatively high temperature rise due to the heat converted from plastic work, especially under impact loading. In this study, a series of compression tests for β-titanium alloy in the wide ranges of testing temperature (77K∼673K) and strain rate (3.3 × 10-4∼103s-1) was carried out to investigate the effect of the heat generation on the mechanical properties. The temperature rise of the specimen during impact compression tests was measured by an infrared radiation thermometer with a photoconductive element. The conversion ratio of plastic work into heat βh was also examined at temperatures of 201K∼473K. The principal results obtained are as follows: The temperature rise of specimen during plastic deformation at 201K is greater than that observed at room temperature (298K) and at 473K. The conversion ratio βh is not necessarily to be constant, i.e. βh is less than 0.1 in the early plastic deformation and gradually increases up to around 0.7 with the increase of plastic deformation at 298K. The increase of βh at lower temperature is more drastic.
収録刊行物
-
- 材料
-
材料 62 (9), 562-568, 2013
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680421930752
-
- NII論文ID
- 130004481094
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BC3sXhslyntb%2FK
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 024897409
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可