<b>Alcohol-Liquefied Wood-Based Epoxy Resins </b><b>- Relation between the Biomass Content and the Mechanical Properties </b>
-
- AkaMatsu Yuki
- Graduate School of Engineering, University of Hyogo Nagase ChemteX Corporation
-
- Fujiwara Taichi
- Graduate School of Engineering, University of Hyogo
-
- Noguchi, Masayuki
- Graduate School of Engineering, University of Hyogo
-
- Nishida Hirofumi
- Nagase ChemteX Corporation
-
- Matsuda Satoshi
- Graduate School of Engineering, University of Hyogo
-
- kishi Hajime
- Graduate School of Engineering, University of Hyogo
Bibliographic Information
- Other Title
-
- <b>アルコール液化木材エポキシ樹脂のバイオマス含有率と力学特性 </b>
- アルコール液化木材エポキシ樹脂のバイオマス含有率と力学特性
- アルコール エキカ モクザイ エポキシ ジュシ ノ バイオマス ガンユウリツ ト リキガク トクセイ
Search this article
Abstract
SynopsisThe glass transition temperatures(Tgs) and tensile properties of the alcohol-liquefied wood-based epoxy resins were studied in relation to the biomass content in the resins. Firstly, the planet-type ball-mill crushing was conducted to the wood powder as a pretreatment of the wood liquefaction. The pretreatment was effective to break the crystalline structure of the cellulose in the wood. As the results, the biomass content in the alcohol-liquefied wood was increased to 63wt%. After that, wood-based epoxy resins were synthesized from the alcohol-liquefied wood with various biomass contents. The Tgs, the tensile strengths and the tensile moduli of the cured wood-based epoxy resins increased with increasing the biomass content in the resins. The rigid chemical structure of the wood-derived molecules would result in the high Tgs and the high mechanical properties of the wood-based epoxy resins.(Received January 5, 2011 ; Accepted February 10, 2011)
Journal
-
- Journal of Network Polymer,Japan
-
Journal of Network Polymer,Japan 32 (2), 83-88, 2011
Japan Thermosetting Plastics Industry Association
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680438125184
-
- NII Article ID
- 130004648249
- 40018764988
-
- NII Book ID
- AN10521608
-
- COI
- 1:CAS:528:DC%2BC3MXkvFehtr4%3D
-
- ISSN
- 2186537X
- 13420577
-
- NDL BIB ID
- 11040436
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed