- S0420202 Degradation and deformation of carbon phenolic ablator under elevated temperature : About the Use of the JSME Specification Template File
説明
The degradation and deformation of an ablator made of carbon fiber reinforced phenolic resin was observed after arc-plasma wind tunnel tests. The observation revealed the delamination was generated inside material and it caused the expansion in an out-of-plane direction. Under such a rapid heating condition, the thermal stress is induced inside material. In order to simulate the thermal stress inside material heated by the arc wind tunnel tests, temperature distributions and thermal stresses were calculated using simulation software: ABAQUAS. The thermal stress compressed in the in-plane direction by 10〜11 MPa which is close to the compressive strength of it. Consequently, the delamination observed after heating resulted from the rapid one-dimensional heating generating the thermal stress.
収録刊行物
-
- 年次大会
-
年次大会 2014 (0), _S0420202--_S0420202-, 2014
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680821238400
-
- NII論文ID
- 110009945084
-
- ISSN
- 24242667
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可