OS0608 FGA Formation Mechanism of Bearing Steel in Rotating Bending Fatigue Test under Decreased Loads
-
- OGUMA Noriyasu
- Faculty of Engineering, University of Toyama
-
- SAKAI Tatsuo
- 立命館大学
-
- WATANABE Koichi
- 株式会社不二越
-
- ODAKE Yasuhiro
- 株式会社不二越
Bibliographic Information
- Other Title
-
- OS0608 軸受鋼の応力漸減回転曲げ疲労試験におけるFGA形成機構(OS6-2 内部破壊とそのメカニズム,OS-6 金属材料の超高サイクル疲労と信頼性評価)
Abstract
In order to examine the fine granular area (FGA) formed timing in under rotating bending fatigue for high strength steel, the rotating bending tests were carried out under decreased loads for bearing steel. The decreased loads were three conditions, the ratio of cumulative number of stress cycles at the high stress level were 2, 4, 7% against the average of the fatigue life in the interior inclusion induced fracture, and were 80% against the average of the fatigue life in the surface induced fracture. From the experimental results, FGA was observed around the inclusion. The size of FGA and the stress intensity factor range of FGA were almost similar to each other for every condition.
Journal
-
- The Proceedings of the Materials and Mechanics Conference
-
The Proceedings of the Materials and Mechanics Conference 2011 (0), _OS0608-1_-_OS0608-3_, 2011
The Japan Society of Mechanical Engineers
- Tweet
Details 詳細情報について
-
- CRID
- 1390282680848116352
-
- NII Article ID
- 110009689642
-
- ISSN
- 24242845
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed