OS1001 軸受鋼の回転曲げ疲労特性に及ぼす水素と残留応力の相互影響

DOI Web Site

書誌事項

タイトル別名
  • OS1001 Interrelated Influence of Hydrogen and Residual Stress on Fatigue Characteristics of Bearing Steel in Rotating Bending

抄録

Rotating bending fatigue tests of hydrogen-charged bearing steels with high compressive residual stress in a specimen surface were carried out. The fatigue life of specimen with compressive residual stress was improved, when hydrogen-charged one was declined. Based on SEM observations of fracture surfaces, the inclusion sizes of the later specimens were similar to the former specimens and the crack initiation sites were deeper. The fatigue life was shorter although stress amplitude at inclusion site was small, so it is presumed that crack propagation rate was further accelerated by compressive residual stress.