Removal of Sulfur from Lead Sulfide by Oxidation-A Fundamental Study on the Recovery of Pb from Lead Blast Furnace Dusts-
-
- MICHIMOTO Tatsuhiko
- Kansai University
-
- KISHIMOTO Atsushi
- Kansai University
-
- WADA Akito
- Kansai University
-
- OISHI Toshio
- Faculty of Engineering, Kansai University
Bibliographic Information
- Other Title
-
- PbSの酸化による脱イオウ―鉛溶鉱炉煙灰からの鉛の回収に関する基礎的研究―
- PbS ノ サンカ ニ ヨル ダツイオウ ナマリ ヨウコウロ エンカイ カラ ノ ナマリ ノ カイシュウ ニ カンスル キソテキ ケンキュウ
- -A Fundamental Study on the Recovery of Pb from Lead Blast Furnace Dusts-
- -鉛溶鉱炉煙灰からの鉛の回収に関する基礎的研究-
Search this article
Abstract
Fundamental study to remove sulfur from PbS was performed by heating PbS under a stream of air at a given temperature between 973 K and 1273 K. Desulfurization ratio was evaluated by measuring the amount of SO2 generated by oxidation reaction and the residual products were analyzed by X-ray diffraction method.<BR>The desulfurization ratio increased with increasing temperature and reached approximately 80 % at 1200 K after 7.2 ks under an air flow rate of 500ml/min. The residual products changed from PbSO4 to PbO through PbSO4·xPbO during heating, where X in PbSO4·xPbO increased with increasing temperature. <BR>SiO2 was added to PbS to promote desulfurization ratio. Mixtures of PbS and SiO2 at various ratios were put under a stream of air at the same experimental condition. At 1073 K, SiO2 showed a remarkable effect on desulfurization at xsio<SUB>2</SUB> < 0.5, where xsio<SUB>2</SUB> denotes mole fraction of SiO2 in PbO-SiO2 system. At xsio<SUB>2</SUB> = 0.3, the desulfurization ratio was approximately 80 % which is equal to the value of the case at 1173 K without SiO2.
Journal
-
- Shigen-to-Sozai
-
Shigen-to-Sozai 122 (3), 129-133, 2006
The Mining and Materials Processing Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681027293184
-
- NII Article ID
- 10017540371
-
- NII Book ID
- AN10062646
-
- COI
- 1:CAS:528:DC%2BD28Xktl2isLg%3D
-
- ISSN
- 18806244
- 09161740
-
- NDL BIB ID
- 7913262
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed