Viability Evaluation using the Effective Thermal Conductivity during Extracellular Freezing in Killifish Embryos.

DOI Web Site Web Site 2 Citations 24 References

Bibliographic Information

Other Title
  • 有効熱伝導率による細胞外凍結におけるヒメダカ受精卵の損傷評価
  • ユウコウ ネツ デンドウリツ ニヨル サイボウガイ トウケツ ニ オケル ヒメ

Search this article

Description

The purpose of this study is to evaluate the correlation between the viability of milliscale biological materials and their effective thermal conductivity during extracellular freezing in order to achieve successful cryopreservation. The killifish embryo (Oryzias latipes, orange-red variety, φ1.3mm sphere) was employed as a sample biological material and the viability was evaluated by the hatching rate. Dimethylsulfoxide-water was selected as the cryoprotectant. The thermal conductivity was measured using a self-heated thermistor technique developed by T. A. Balasubramaniam (1977). The thermistor (φ2.5mm sphere) was installed at the bottom of a test section 8×8×12mm, and exposed to biological material. The cooling system was equipped with Peltier devices and was capable of reducing the temperature of the test section to -30°C. Between 150 and 200 embryos were loaded in the test section with 5, 15 and 20% w/w Dimethylsulfoxide-water. The effective thermal conductivity during extracellular freezing was measured over the temperature range -20 to 6°C with a cooling rate of 0.1 to 10°C/min. The effective thermal conductivity increased from 0.5 to 1W/ (m·K) with decreasing temperature and increasing the cooling rate. The decrease in the hatching rate and the variation in the effective thermal conductivity were correlated. Thus the viability could be controlled using their effective thermal conductivity during the extracellular freezing.

Journal

Citations (2)*help

See more

References(24)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top