書誌事項
- タイトル別名
-
- Evaluation of Stress Corrosion Cracking Susceptibility of Type 304 Stainless Steel by Controlled Potential SSRT
- テイ デンイ SSRT ニ ヨル 304 ステンレス コウ ノ オウリョク フ
この論文をさがす
説明
Stress corrosion susceptibility of Type 304 stainless steel in various concentration of CaCl2 solution has been examined by two types of the slow strain rate technique (SSRT), comparing with time to failure and corrosion potential which had been obtained by the constant load test in the same solution. The SSRT in free corrosion condition and in controlled potential condition was compared. It is concluded that the controlled potential SSRT, the potential of which is simulated to the constant load test, could give more proper index corresponding to time to failure than the conventional type SSRT done in free corrosion condition. But in the lower concentration region below the critical concentration of 25% CaCl2, both type of the SSRT could not cause SCC which had been observed in the constant load test.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 37 (3), 138-143, 1988
社団法人 腐食防食協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681235174400
-
- NII論文ID
- 130004732017
- 130006025142
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 3170841
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可