- Corrosion Behavior of Amorphous and Cry
この論文をさがす
抄録
The corrosion behavior of Ni-Cr-P-C alloys in which the Ni/Cr atomic ratio was fixed to unity was studied in connection with metallurgical structure by electrochemical measurement and X-ray diffraction. The Ni-Cr alloy was vitrifiable by the addition of 12 at% phosphorus, but was not by single addition of carbon. In 6N HCl at 30°C, both conventionally cast and melt-spun crystalline Ni-Cr alloys had low corrosion potentials less than -300mV (SCE) and showed high anodic current density of the order of 103 to 104A/m2 by anodic polarization. Once they were vitrified, they passivated spontaneously in the same aggressive solution and showed excellent corrosion resistance. The corrosion resistance of amorphous alloys was largely deteriorated even by a small amount of crystalline phase precipitation.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 38 (7), 384-389, 1989
社団法人 腐食防食協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681235474176
-
- NII論文ID
- 130004732116
- 130006025231
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 3247671
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可