- Effect of Austenite Phase Content on Pitting Potential of a Duplex Stainless Steel
- 2相ステンレス鋼の孔食電位に及ぼすγ相量の影響
- 2ソウ ステンレス コウ ノ コウショク デンイ ニ オヨボス ガンマソウリョ
この論文をさがす
抄録
In order to examine the effect of γ phase content on pitting potential of a duplex stainless steel, pitting potentials for type 329 J1 duplex stainless steel with the different α/γ phase ratio prepared by isothermal heat treatment in NaCl and NaCl-H2SO4 solutions have been determined by measurements of the anodic polarization curves. The dependence of measured pitting potentials on γ phase content was considered on the basis of the results for the microscopic observation of pit sites on the metal surface and the EPMA analysis of chemical compositions for α and γ phases. When the structure of type 329 J1 steel changed from α single phase to (α+γ) duplex phase, pitting potential in NaCl solution lowered significantly. This lowering of pitting potential corresponded to the change in pitting site from a phase to γ phase. Pitting potentials of type 329 J1 steels with (α+γ) duplex structure decreased slightly with an increase in γ phase content in NaCl and NaCl-H2SO4 solutions. It was considered that such decreases in pitting potentials were attributed to the decrease in chromium content of the transgranular precipited γ phase on which pits generated with an increase in γ phase content.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 36 (10), 650-656, 1987
社団法人 腐食防食協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681236141056
-
- NII論文ID
- 130006025071
- 130004731899
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 3157712
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可