復水器用アルミニウム黄銅管の早期潰食事例についての一考察

DOI Web Site Web Site
  • 山本 博司
    古河金属工業株式会社大阪伸銅所技術部研究開発課
  • 国枝 博
    古河金属工業株式会社大阪伸銅所技術部研究開発課
  • 小山 輝男
    古河金属工業株式会社大阪伸銅所技術部研究開発課
  • 西島 直道
    古河金属工業株式会社本社技術部

書誌事項

タイトル別名
  • Unexpected Impingement Corrosion of Aluminum Brass Condenser Tubes
  • フクスイキヨウ アルミニウム オウドウカン ノ ソウキ カイショク ジレイ ニ

この論文をさがす

抄録

Some discussions about the mechanism of the unexpected severe impingement corrosion of condenser tubes were made in relation to hydrotalcite. It was elucidated experimentally that hydrotalcite is the initial corrosion product of Aluminum Brass in the natural sea water. Even if iron rich protective films are formed on hydrotalcite, they will be broken quite easily by the collision of foreign bodies with smaller energy in the sea water. This will increase the possibility of corrosion. The most important countermeasure is to supress the initial corrosion of condenser tubes by the effective ferrous ion dosing and to prevent hydrotalcite formation. It was pointed out that more attension should be paid to hydrotalcite from the standpoint of corrosion engineering of condenser tubes.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ