10%しゅう酸エッチ試験方法によって検出されるステンレス鋼における粒界鋭敏化の材質要因
書誌事項
- タイトル別名
-
- Material Factors of Grain Boundary Sensitization in Stainless Steels Detected by 10% Oxalic Acid Etching Test Method
説明
Material factors which cause intergranular corrosion (etched grain boundaries) of Type 304 stainless steel in 10% oxalic acid etching and nitric acid-fluoric acid etching test methods are studied. It has been clarified that the material factor of grain boundary etching in 10% oxalic acid etching test is never the Cr depletion at grain boundaries, but the Cr carbide precipitated at GB. Also, it has been found that the Cr depletion at grain boundaries is the only cause for GB etching in nitric acid-fluoric acid etching test and Cr depleted zone is completely healed by the diffusion of Cr from the matrix in the heat treatment at 800°C for more than 250h.
収録刊行物
-
- 材料と環境
-
材料と環境 49 (6), 374-378, 2000
公益社団法人 腐食防食学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681236822272
-
- NII論文ID
- 130004085765
-
- COI
- 1:CAS:528:DC%2BD3cXkt1ylurc%3D
-
- ISSN
- 18819664
- 09170480
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可