Effects of pH and Applied Potential on the IGSCC Susceptibility of Sensitized Type 304 Stainless Steel in Dilute Na<sub>2</sub>SO<sub>4</sub> Solution at High Temperature
-
- Fujiwara Kazuo
- Central Research Laboratory, Kobe Steel Ltd.
-
- Tomari Haruo
- Central Research Laboratory, Kobe Steel Ltd.
-
- Shimogori Kazutoshi
- Central Research Laboratory, Kobe Steel Ltd.
-
- Fukuzuka Toshio
- Central Research Laboratory, Kobe Steel Ltd.
Bibliographic Information
- Other Title
-
- 高温稀薄Na<sub>2</sub>SO<sub>4</sub>水溶液中における鋭敏化304ステンレス鋼の粒界応力腐食割れに及ぼすpHおよび印加電位の影響
- 高温稀薄Na2SO4水溶液中における鋭敏化304ステンレス鋼の粒界応力腐食割れに及ぼすpHおよび印加電位の影響
- コウオン キハク Na2SO4 スイヨウエキチュウ ニ オケル エイビンカ 3
Search this article
Description
The effects of pH and applied potential on the IGSCC of sensitized Type 304 SS were studied in dilute Na2SO4 solution at 285°C in connection with the polarization behaviors, in order to clarify the roles of crevice and dissolved oxygen in the evaluation of SCC susceptibility with double U-bend specimen in high temperature water. The results are summarized as follows. (1) The role of dissolved oxygen in the IGSCC behavior of sensitized Type 304 SS, is to make the potential of the steel noble. On the other hand, in the deaerated solution this same role was proved to be played by externally-applied potential, which is as noble as in the aerated solution. (2) The IGSCC in the inner specimen of double U-bend is caused by the environmental change inside the crevice, where the pH value is lowered to less than 3 due to the hydrolysis of metallic ions dissolved from the specimen, and by the potential shift of inner specimen to the transition region from an active to a passive state on the locar cell anodic polarization curve, where IGSCC can readily be generated.
Journal
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 30 (5), 270-275, 1981
Japan Society of Corrosion Engineering
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681237003392
-
- NII Article ID
- 130006024699
- 130004731426
-
- NII Book ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL BIB ID
- 2315818
-
- Data Source
-
- JaLC
- NDL Search
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed