Synthesis and Properties of Polyaniline/Sodium and Zinc Ionomer Composites.

DOI Web Site 参考文献40件
  • Wang Yuming
    Chemistry Department, Huazhong University of Science and Technology
  • Xie Hongquan
    Chemistry Department, Huazhong University of Science and Technology
  • Cai Ying
    Chemistry Department, Huazhong University of Science and Technology
  • Guo Junshi
    Chemistry Department, Huazhong University of Science and Technology

書誌事項

タイトル別名
  • Synthesis and Properties of Polyaniline

この論文をさがす

抄録

Polymerization of aniline was carried out with stable poly(methyl methacrylate-butyl methacrylate-sodium acrylate) [P(MMA-BA-AANa)] and poly(methyl methacrylate-butyl methacrylate-zinc acrylate) [P(MMA-BA-(AA)2Zn)] ionomer emulsions to improve the processability of polyaniline (PANI). The results indicated that the two ionomer emulsions not only improved the tensile strength of PANI but also maintained the conductivity of PANI at room temperature. Suitable polymerization conditions had been established for the synthesis of PANI/P(MMA-BA-AANa) and PANI/P(MMA-BA-(AA)2Zn) composites. The obtained PANI composites had the conductivity of more than 10 S cm−1 with tensile strength of more than 7.0 MPa at room temperature. The threshold values were proved to be 19 w/w% and 16 w/w% for PANI/P(MMA-BA-AANa) and PANI/P(MMA-BA-(AA)2Zn) composites, respectively.

収録刊行物

  • Polymer Journal

    Polymer Journal 29 (11), 875-880, 1997

    The Society of Polymer Science, Japan

参考文献 (40)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ