- Synthesis and Properties of Polyaniline
この論文をさがす
抄録
Polymerization of aniline was carried out with stable poly(methyl methacrylate-butyl methacrylate-sodium acrylate) [P(MMA-BA-AANa)] and poly(methyl methacrylate-butyl methacrylate-zinc acrylate) [P(MMA-BA-(AA)2Zn)] ionomer emulsions to improve the processability of polyaniline (PANI). The results indicated that the two ionomer emulsions not only improved the tensile strength of PANI but also maintained the conductivity of PANI at room temperature. Suitable polymerization conditions had been established for the synthesis of PANI/P(MMA-BA-AANa) and PANI/P(MMA-BA-(AA)2Zn) composites. The obtained PANI composites had the conductivity of more than 10 S cm−1 with tensile strength of more than 7.0 MPa at room temperature. The threshold values were proved to be 19 w/w% and 16 w/w% for PANI/P(MMA-BA-AANa) and PANI/P(MMA-BA-(AA)2Zn) composites, respectively.
収録刊行物
-
- Polymer Journal
-
Polymer Journal 29 (11), 875-880, 1997
The Society of Polymer Science, Japan
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681264555648
-
- NII論文ID
- 130004429819
- 10006273258
-
- NII書誌ID
- AA00777013
-
- COI
- 1:CAS:528:DyaK2sXnsFWgtr0%3D
-
- ISSN
- 13490540
- 00323896
-
- NDL書誌ID
- 4346265
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可