- Effect of Ba Addition to the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System. (V).
- Bi Pb Sr Ca Cu Oケイ コウオンソウ エ ノ Ba テンカ コウ
この論文をさがす
抄録
The effects of cooling condition and Ba addition time on Tc of high-Tc phase in the Bi-Pb-Sr-Ca-Cu-O system were studied. X-ray diffraction and DC resistance measurements were carried out to observe phase identification and Tc values for a series of samples with compositions of Bi:Pb:Sr:Ba:Ca:Cu=0.9:0.2:1.0:X:1.0:1.6(X=0-0.05). When a mixture of BaCO3 and synthesized high-Tc phase was heated at 850°C for 60h in air, only a solid solution of high-Tc phase was formed in a quenched sample. However, in a sample cooled down slowly, Bi3(Sr, Ba)4Ca3Oz was found as an impurity phase in addition to the solid solution of high-Tc phase. Mixtures of BaCO3 (X=0.04) and the rest of metal oxides or metal carbonates were heated at 845°C 96h in air. Bi3(Sr, Ba)4Ca3Oz was also found in addition to the high-Tc phase in a quenched sample. When BaCO3 was added to the synthesized high-Tc phase, Tc(R=0) was 119K for the heated samples. When BaCO3 was added in starting materials, Tc decreased to 110K due to the formation of Bi3(Sr, Ba)4Ca3OZ.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 39 (5), 374-377, 1992
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681281383552
-
- NII論文ID
- 130000818168
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3769700
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可