Effect of Li-addition to the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System. (II).
-
- Takada Jun
- Department of Applied Chemistry, Faculty of Engineering, Okayama University
-
- Fujiwara Masashi
- Department of Applied Chemistry, Faculty of Engineering, Okayama University
-
- Egi Toshio
- Department of Applied Chemistry, Faculty of Engineering, Okayama University Superconducting and Cryogenic Technology Center, Kobe Steel, Ltd.
-
- Nanba Tokuro
- Department of Applied Chemistry, Faculty of Engineering, Okayama University
-
- Ikeda Yasunori
- Institute for Chemical Research, Kyoto University
-
- Takano Mikio
- Institute for Chemical Research, Kyoto University
-
- Mazaki Hiromasa
- Department of Mathematics and Physics, The National Defence Academy
Bibliographic Information
- Other Title
-
- Bi‐Pb‐Sr‐Ca‐Cu‐O系高温相へのLi添加効果 (第II報)
- Bi Pb Sr Ca Cu Oケイ コウオンソウ エ ノ Li テンカ コウ
Search this article
Abstract
The effects of Li-addition to the high-Tc phase in Bi-Pb-Sr-Ca-Cu-O system have been studied for the samples with the nominal composition of Bi:Pb:Sr:Ca:(Cu, Li)=0.96:0.24:1.0:1.1:(1.6-x, x) heated at 840 to 845°C for 144h in air (x=0 to 0.2). The characterization of the samples has been made by DTA, the measurements of XRD and DC electrical resistivity, SEM observation and ICP analysis. The Li-addition promotes the formation of the high-Tc phase. The sample with x=0.05 heated at 842°C for 144h exhibits Tc=116K, while Tc=109K for the Li-free sample (x=0) heated at 842°C for 120h. The results of ICP analysis showed that the Li content of the samples heated at 842°C for 120h was very low.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 39 (5), 386-389, 1992
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681281385088
-
- NII Article ID
- 130000818178
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3769703
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed