書誌事項
- タイトル別名
-
- Reactions of TiO2 and BaCO3 with a CO2 Laser.
- TiO2 ト BaCO3 ノ CO2 レーザー ニ ヨル ハンノウ
この論文をさがす
抄録
The report describes the solid reaction between TiO2 and BaCO3 under a CO2 laser irradiation. The powders of TiO2 and BaCO3 are mixed for a compaction and the green pellets (thickness; 0.95mm) were irradiated with the powers of 1.14, 1.40, 1.85 and 2.14 kW/cm2. The temperatures were 1053-1500 K depending on the laser powers. The laser power more than 1.85 kW/cm2 led to the sintered body from the green pellet. The formation of BaTiO3 was identified with X-ray diffraction analysis. The scanning electron microscopy revealed that the product was the porous ceramics with necking between grains. The sintered density was as low as 60-70% TD. The permittivity of BaTiO3 after irradiation at 2.14 kW/cm2 was 80 approximately.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 40 (5), 541-544, 1993
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681282979328
-
- NII論文ID
- 130000819258
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3825454
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可