Preparation and Mechanical Property for WC-25vol%FeAl Using Wet Milling Process
-
- Matsumoto Akihiro
- Materials Research Institute of Sustainable Development, National Institute of Advanced Industrial Science and Technology
-
- Kato Kiyotaka
- Materials Research Institute of Sustainable Development, National Institute of Advanced Industrial Science and Technology
-
- Shimojima Koji
- Materials Research Institute of Sustainable Development, National Institute of Advanced Industrial Science and Technology
-
- Hosokawa Hiroyuki
- Materials Research Institute of Sustainable Development, National Institute of Advanced Industrial Science and Technology
-
- Takada Masayuki
- Nippon Tokushu Goukin Co., Ltd.
-
- Hiramatsu Takashi
- Nippon Tokushu Goukin Co., Ltd.
Bibliographic Information
- Other Title
-
- 湿式混合を利用したWC-25vol%FeAlの作製と機械的特性
- シッシキ コンゴウ オ リヨウ シタ WC 25vol% FeAl ノ サクセイ ト キカイテキ トクセイ
Search this article
Abstract
WC-25vol%FeAl compacts have been prepared using wet milling and the subsequent pulse current sintering. Powder mixtures consisting of (1) WC, Fe-40at%Al and (2) WC, Fe, Al powders have been mixed to give the desired composition of WC-25vol%FeAl. They have been milled using a cylindrical ball mill with ethanol. Milled powders have been dried at room temperature and consolidated using pulse current sintering method at 1273 K in vacuum. The compacts thus obtained have had fine and homogeneous structure. Vickers hardness of both compacts has increased with increasing milling time. Transverse rupture strength of the former compact has increased with increasing milling time, but that of the latter one abruptly decreased. This is due to the formation of Fe3W3C and Al-O phase.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 57 (12), 764-768, 2010
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681283558144
-
- NII Article ID
- 10027756514
-
- NII Book ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3MXhtFWjtbc%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 10949531
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed