Effect of wire dialmeter on particle size of metal nanosized powder prepared by pulsed wire discharge
-
- Tokoi Yoshinori
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Suzuki Tsuneo
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Nakayama Tadachika
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Suematsu Hisayuki
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Jiang Weihua
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Niihara Koichi
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
書誌事項
- タイトル別名
-
- Effect of Wire Diameter on Particle Size of Metal Nanosized Powder Prepared by Pulsed Wire Discharge
この論文をさがす
抄録
Copper, silver and nickel nanosized powders were prepared using metal wires with different diameters in nitrogen gas by pulsed wire discharge. The diameter of the wire was changed from 0.05 to 0.3 mm. The pressure of nitrogen and charged energy were fixed at 100 kPa and 540 J, respectively. After the discharge of the wires, the volume of plasma/vapor measured by high-speed photographs was almost constant even though the wire diameter was changed. On the other hand, the median diameter of copper, silver and nickel nanosized powders was decreased with decreasing the diameter of the wire. Therefore, the decrease in the median diameter accompanies the decrease in the density of the plasma/vapor.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 55 (3), 192-197, 2008
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681283686272
-
- NII論文ID
- 10021172898
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD1cXjvFCitLg%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 9436638
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可