Pure magnesium powders were mechanically alloyed with addition powders of low-melting-metal oxides (SnO2, PbO and Sb2O3) by using a planetary ball mill under an Ar atmosphere. After mechanical alloying, the powders were consolidated to the P/M materials by vacuum hot pressing. Solid state reaction in the mechanically alloyed powders and the P/M materials was studied by XRD and DSC. In these systems, the solid state reaction started to occur during MA processing between Mg and low-melting-metal oxides. The added low-melting metal oxides decomposed and formation of MgO and intermetallic compounds (Mg2Sn, Mg2Pb, Mg3Sb2) occurred. Such solid state reaction further progressed during hot-pressing and subsequent heat treatment. Microstructures were studied by TEM and mechanical strength was discussed by hardness values for both MA powders and P/M materials.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 48 (5), 397-403, 2001
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681283919616
-
- NII論文ID
- 10007482913
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD3MXksF2gtro%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 5773286
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可