Non-shrinkage Alumina Material.
-
- Inuzuka Tsutomu
- Corporate Components Development Center, Matsushita Electronic Components Co., Ltd.
-
- Tomioka Satoshi
- Corporate Components Development Center, Matsushita Electronic Components Co., Ltd.
-
- Harada Shinji
- Corporate Components Development Center, Matsushita Electronic Components Co., Ltd.
Bibliographic Information
- Other Title
-
- 無収縮アルミナ材料
- ム シュウシュク アルミナ ザイリョウ
Search this article
Abstract
To fabricate a sintered Al2O3 with high dimensional accuracy by near-net-shape firing, oxidation and sintering behavior of compacts of a mixture of Al2O3 and Al powders was studied. The compacts were prepared by compressing green-sheets obtained by doctor-brade method at 196MPa and fired at 1600°C or less in air. The oxidation of Al in the compact occured between about 450°C and 1300°C, and prevents the compact from shrinking in firing process at 1300°C or less. A part of melting Al in the compact spilled out of the compact in firing process, because Al melts below 800°C, its oxidation temperature. MgO, CaCO3 and TiO2 powders were added to prevent the Al spillage and Si powder was added to prevent the shrinkage by sintering at 1400°C or more. As a result, the sinterd Al2O3 having a density of 3.72g/cm3 and 0.7% shrinkage by sintering was fabricated by sintering with oxidation of Al and formation of mullite.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 44 (8), 729-733, 1997
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681283923456
-
- NII Article ID
- 10002014358
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 4275736
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed