Joining of SUS316L and SUS430L Stainless Steel Parts with the Paste Containing Stainless Steel Powder in MIM Process
-
- Satoh Kenji
- Hamamatsu Industrial Research Institute of Shizuoka Prefecture
-
- Itoh Yoshinori
- Hamamatsu Industrial Research Institute of Shizuoka Prefecture
-
- Harikoh Tatsuya
- Hamamatsu Industrial Research Institute of Shizuoka Prefecture
-
- Miura Hideshi
- Guraduate School of Kumamoto University
Bibliographic Information
- Other Title
-
- 自動車焼結部品における新しい技術と展開 ステンレス鋼粉末含有ペースト糊によるＳＵＳ３１６ＬおよびＳＵＳ４３０Ｌ射出成形品の接合
- ステンレス コウフンマツ ガンユウ ペーストノリ ニ ヨル SUS316L オヨビ SUS430L シャシュツ セイケイヒン ノ セツゴウ
Search this article
Abstract
The combinations of the same stainless steels (SUS316L/SUS316L, SUS430U/SUS430L) and the different stainless steels (SUS316L/SUS430L) were joined with the pastes containing the stainless steel powder in MIM process. For joining the same stainless steels, the values of joined strength were 400MPa for SUS316U/SUS316L compact sintered at 1623 K, and 320 MPa for SUS430L/USUS430L compact sintered at 1373 K respectively.<BR>For joining the different stainless steels, the values of joined strength for SUS316L/SUS430L compacts sintered at 1623 K were 330 MPa by using the paste with SUS316L, and 370 MPa by using the paste with SUS430L.<BR>At the joined area of SUS316L/SUS430L sintered compacts, the mixed layer (over 100μm thickness) of ferrite and martensite phases was observed.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 50 (7), 566-570, 2003
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681284171008
-
- NII Article ID
- 10011242471
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 6654618
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed