- アルミナの射出成形 脱脂機構の検討
- アルミナ ノ シャシュツ セイケイ ダッシ キコウ ノ ケントウ
- Characterization of Debinding Process
- 脱脂機構の検討
Search this article
Description
The Alumina powder mixed the each organic binder(A, B, C) were molded rod like test pieces by a screw injection-molding machine. The binder(A) consisted of polystylene (PS), polybutylmethacrylate(PBMA), stearic acid(St) and paraffin wax(WAX); (B) consisted of PS, PBMA, St, WAX and atactic polypropylene(APP); (C) consisted of PS, PBMA, St, APP. The test pieces which were made of the binder(B), (C) cracked easily during the debinding process, but those which was made of the binder(A) didn't crack. From the above fact, one of the reasons was shown that owing to the radical thermal decomposition of the APP at the about 200°C, the rate of debinding of the binder(B), (C) were rapider than that of binder(A). So that it was clear that the causing cracks within the test pieces resulted from the rising rate of debinding at about 200°C.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 36 (2), 174-177, 1989
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681284347264
-
- NII Article ID
- 130000813540
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3236116
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed