セラミック系高温超伝導体の合成と評価

DOI Web Site

書誌事項

タイトル別名
  • Synthesis and characterization of high TC superconducting ceramics.
  • セラミックケイ コウオン チョウデンドウタイ ノ ゴウセイ ト ヒョウカ

この論文をさがす

説明

Twelve compositions of high Tc superconducting ceramic materials, with the compositios Ba2YCu3O7-δ and Ba2LnCu3O7-δ (Ln=La, Nd, Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Lu) were synthesized and studied. The authors have focused their studies on the ortho-tetra phase transition in the lanthanide compounds as well as the yttrium compound. The orthorhombic-tetragonal Ba2YCu3O7-δphase boundary in the δ-T daiagram was determind by the detailed isobar thermogravimetric(TG) measurement under the oxygen parial pressures of 1 to 0.01 atm. The transition temperatures of the lanthanide compounds were also measured. It was found that the, transition temperatures depend on the length of the a and b axis in the unit cell. A simple model considering a repulsion energy between oxygen atoms in the c plane was proposed, explaining trends in transition temperature and oxygen content.<BR>Thick film and green sheet powder processing techniques have been studied, with application to electronic components and devices. A paste of calcined powder was made and screen-printed on various substrates. The Tcend was found to be 87K for yttria-stabilized-zirconia substrate. The ceramic body made using green sheet process had the same properties as those of the sample made using conventional powder processing techniques.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ