- Fibre metallurgical processing of cast iron-graphite composite material for self-lubrication service.
- チュウテツ コクエンケイ ジコ ジュンカツ フクゴウ ザイリョウ ノ センイ
この論文をさがす
説明
For further development of the high performance self-lubrication materials being proof against vacuum or high temperature, cast iron fibre composites containing a large amount of graphite were investigated. The cast iron fibre of 20-40 μm in diameter and 1.2 mm in length, which was prepared by chatter-machining a ductile cast iron bar, was mixed with graphite powder and consolidated by compacting in a die, sintering and finally repressing. The optimum conditions for the processing were determined experimentally, and the composite of the almost same mechanical strength as grey iron was made with an addition of 28.8 vol% graphite. In conclusion the fibre metallurgical processing of the high performance self-lubrication composite materials of cast iron and graphite is feasible in the production.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 35 (6), 552-557, 1988
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284456704
-
- NII論文ID
- 130000813353
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3651204
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可