Perovskite Formation Process in Pb(Ti⋅Zr)O<SUB>3</SUB> Ceramics Containing SiO<SUB>2</SUB>

DOI Web Site

Bibliographic Information

Other Title
  • Perovskite formation process in Pb(Ti・Zr)O3 ceramics containing SiO2
  • Perovskite Formation Process in Pb(Ti⋅Zr)O3 Ceramics Containing SiO2

Search this article

Description

Influence of SiO2 addition on formation process of Pb(Ti⋅Zr)O3 solid solution was studied. Powdered PbO, TiO2, ZrO2 and SiO2 were used as raw materials. The process was determined from the variation of X-ray diffraction patterns and that of dilatometric dimensional change with heating temperatures.<BR>If the materials excluding SiO2 were mixed, Pb(Ti⋅Zr)O3 was synthesized, passing through formations both of PbTiO3 and PbZrO3. However, when the materials including SiO2 were mixed, the PbZrO3 formation was suppressed, accompanying by a decrease of Pb(Ti⋅Zr)O3 formation temperature.<BR>The difference seems to be caused by the appearance of a liquid phase formed by the co-existence of SiO2 and PbO, which occurs during the Pb(Ti⋅Zr)O3 formation process. Reaction observed at the contact surface of two green compacts, consisting of SiO2-PbO as well as of Pb(Ti⋅Zr)O3, was in line with the assumption.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top