Mechano-chemical Synthesis of Lithium Ion Conducting Materials in the System Li2O-Li2S-P2S5
-
- Machida Nobuya
- Department of Chemistry, Konan University
-
- Yoneda Yuki
- Department of Chemistry, Konan University
-
- Shigematsu Toshihiko
- Department of Chemistry, Konan University
この論文をさがす
抄録
Amorphous solid electrolytes were prepared in the compositions 75 {(1-x)Li2O⋅xLi2S}⋅5P2S5 (mol%) by using a high-energy ball-milling process. The amorphous materials showed lithium ion conductivities higher than 10-3 Sm-1 at room temperature. The amorphous 7.5Li2O⋅67.5Li2S⋅5P2S5 (mol%) sample showed the highest lithium ion conductivity σ298K=2.7×10-2 Sm-1 at room temperature among the obtained samples. An all-solid-state battery was assembled by using the amorphous 7.5Li2O⋅67.5Li2S⋅5P2S5 sample as solid electrolytes. In the battery, TiS2 and Li4.4Si were employed as positive and negative electrode materials, respectively. The discharge-charge cycling test of the battery was carried out at room temperature under a constant current density of 64μAcm-2 with the discharge-charge criteria of voltages 1.1 and 2.6 V. The battery showed successive reversibility with a large specific capacity; the specific capacity calculated on the base of the weight of the TiS2 positive electrode materials was about 170 mAhg-1.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 51 (2), 91-97, 2004
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284936448
-
- NII論文ID
- 10012105513
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD2cXjtVSmu7o%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL書誌ID
- 6873268
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可