Sinter Joining Properties of Ferrite Magnets.
-
- Okimoto Kunio
- Setsunan University
-
- Izumi Katsuhisa
- Graduate School, Setsunan University
-
- Satoh Tomio
- Kyushu National Industrial Research Institute
-
- Toyota Sachio
- Sumitomo Special Metals Co. Ltd.
-
- Hosokawa Seiichi
- Sumitomo Special Metals Co. Ltd.
Bibliographic Information
- Other Title
-
- 焼結接合法によるフェライト部品の作製
- ショウケツ セツゴウホウ ニ ヨル フェライト ブヒン ノ サクセイ
Search this article
Abstract
For the purpose of fabricating ferrite part with a complicated shape which has different orientation of the ferrite, joining of pre-formed green compacts was studied, and in particular the feasibility of combined sinter joining method was investigated. As the first step, two simple compacts of disk and ring shape have been individually produced under the non-magnetic field condition. The two compacts was assembled into a unit and then sintered at 1150°C and 1225°C. Effect of addition agent and sintering temperature on the joint strength of the the sintered compacts has been studied. The joint strength of the compacts sintered at 1225°C was about 2 times of that of the compacts sintered at 1150°C. The maximum joint strength was obtained when an inner disk with 0.75mass%CaO and an outer ring with 0.75mass%CuO was joined at sintering temperature of 1225°C.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 45 (8), 763-768, 1998
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681285070464
-
- NII Article ID
- 10002052631
-
- NII Book ID
- AN00222724
-
- COI
- 1:CAS:528:DyaK1cXmtFGju7c%3D
-
- ISSN
- 18809014
- 05328799
- http://id.crossref.org/issn/05328799
-
- NDL BIB ID
- 4540070
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed