- Preparation of Fe4N Sintered Compact by HIP.
- HIPホウ ニ ヨル Fe4N ショウケツタイ ノ サクセイ
この論文をさがす
説明
Fe4N powder, which is known as a softmagnetic material, was sintered by Hot Isostatic Pressing (HIP). The powder was obtained by heating a carbonyl iron powder at 500°C for 4h in the mixture of H2-NH3(60vol%). Then, the Fe4N powder was encapsulated into an Al tube in troidal shape. Hipping was performed below 500°C to prevent the decomposition of Fe4N. Single phase Fe4N compact with 99% relative density was obtained under the condition of 450°C, 200MPa and 120min. The saturation magnetization of the compact was 150emu/g.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 41 (8), 989-993, 1994
一般社団法人 粉体粉末冶金協会