- Core losses of Mn-Zn Ferrites with Fine Grain Size.
- ビサイ ナ ケッショウ リュウケイ オ モツ Mn Zn フェライト ノ テッ
この論文をさがす
抄録
Mn-Zn ferrite with fine grains of about 2.1μ m in size was synthesized by sintering of hydrothermal-precipitated ferrite powders, and its core losses were evaluated. At room temperature, based on the dependence of frequency, the core losses of the ferrite at 0.2MHz to 2MHz with 50mT and at 0.5MHz to 5MHz with 5mT are smaller than those of the commercial ferrites with grains of 7.7 μ m to 10.9 μm in size. So, the core loss is 70% at 500kHz, 50mT and 50% at 1MHz, 5mT of that of the commercial ferrites, respectively. At 80°C, which is almost actual circumstance, the core loss of the ferrite is also smaller than that of the commercial ferrite at 0.5MHz to 1MHz. Therefore, the fine grain ferrite is expected to be useful as material for high-frequency transformer.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 40 (9), 877-880, 1993
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285217408
-
- NII論文ID
- 130000819359
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3837257
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可