Development of bronze-type sintered bearing for high speed revolution applications.
-
- Kohno Tohru
- 三菱金属(株)中央研究所
Bibliographic Information
- Other Title
-
- 高速回転用青銅系焼結含油軸受の開発
- コウソクカイ テンヨウ セイドウケイ ショウケツ ガンユ ジクウケ ノ カイハ
Search this article
Description
It was known in the first fundamental study that in the light load and very high speed revolution region (2-6 kg/cm2, above 20, 000 rpm), sintered bearings could be driven under hydrodynamic lubrication after achieving sufficiently good conformity. In the actual applications, however, the state of the lubrication at the start-up becomes a severe boundary owing to insufficient conformity, consequently a large amount of wear occurs or the bearings may seize.<BR>On the basis of the above-mentioned study, a new Cu-Sn-P-MoS2 type bearing has been developed, which showed excellent performance under both boundary and hydrodynamic conditions. The distinctive features of the bearing are as follows; the thin layer of the reaction product (phosphorus compound) formed around the MoS2 particles in the sintered structure acted as a kind of binder between the matrix and the MoS2 particles, thus preventing the solid lubricant (MoS2) from mixing into the lubricant oil, which causes the increase in the apparent viscosity of the oil and consequently the coefficient of friction and the bearing temperature under the hydrodynamic conditions.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 36 (4), 345-351, 1989
Japan Society of Powder and Powder Metallurgy
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681285336320
-
- NII Article ID
- 130000813616
- 10009740550
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 3231639
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed