書誌事項
- タイトル別名
-
- On the Sintering of the TiNx-Ni Binary Mixed Powder Compacts
- TiNX Niケイ コンゴウ アップンタイ ノ ショウケツ トクセイ ニ ツイ
この論文をさがす
抄録
Sintering characteristics of TiNx-Ni mixed powder compacts were studied by heating them in gas atmospheres of nitrogen, hydrogen or argon, or in vacuum.<BR>The shrinkage during sintering was considerably disturbed by the liberated nitrogen gas from the compacts, whereas in lower value for x of TiNx, the gas diffused into TiN, grains up to TiN0.99 without denitrification. So that the shrinkage was remarkably promoted not only in vacuum, but also in hydrogen and argon. While, the nitrogen atmosphere hindered the shrinkage.<BR>The Ni concentration and x value in formula TiNx showing the maximum sintered density in the sintering condition at 1500°C for 60min. were approximately 15 wt% and 0.8, respectively.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 26 (4), 143-148, 1979
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285554688
-
- NII論文ID
- 130000821750
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 2055948
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可