- Oxidation Resistance and Corrosion Resistance of Molybdenum-Chromium Nitride Layer
- Mo Crケイ チッカブツ ヒマク ノ タイサンカセイ ト タイショクセイ
この論文をさがす
説明
For Mo-Cr nitride layer prepared by NH3 gas nitriding of pure Mo subjected to Cr-diffusion treatment, the oxidation behavior in air and corrosion behavior in boiling sulfuric acid were investigated. The surface nitride layer consisted of γ-Mo2N type solid solution of which Mo-Cr ratio was almost 1 : 1 on the surface. Although γ-Mo2N layer obtained by nitriding pure Mo was oxidized at temperatures above 773 K, Mo-Cr nitride layer exhibited superior oxidation resistance up to 1073 K. The corrosion resistance of Mo-Cr nitride layer in boiling sulfuric acid was as excellent as that of γ-Mo2N layer.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 56 (8), 529-533, 2009
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285771904
-
- NII論文ID
- 10025399050
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD1MXhtVaqtb7P
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 10356793
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可