- Hojo Junichi
- Department of Applied Chemistry, Faculty of Engineering, Kyushu University
-
- Champagne Blaise
- Industrial Materials Research Institute, National Research Council of Canada
-
- Dallaire Serge
- Industrial Materials Research Institute, National Research Council of Canada
書誌事項
- タイトル別名
-
- Preparation of Metal Coated Ceramics Pa
この論文をさがす
説明
Ceramics particles of Al2O3 and SiC (mean diameter:'40-770μm) were coated with fine metal particles of Al, Ni, Co, Mo and W (mean diameter: 5-10μm) by the agglomeration coating technique in which ceramics particles containing polyethylene glycol as binder were mixed with metal particles in a rotating cylinder and heated above the melting point of polyethylene glycol so that metal particles were fixed on the surface of ceramics particles by the molten binder. The quantity of metal coating reached a maximum of about 60 vol%. Coarser ceramics particles attained a larger quantity of metal coating. The addition of Al-stearate to metal particles was effective to disperse metal particles and increase the surface coverage of the coating.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 36 (4), 411-417, 1989
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681285832448
-
- NII論文ID
- 130000813619
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3234177
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可