Effects of Pr6O11 Additives on Magnetic Properties and Microstructure of Mn-Zn Ferrites.

DOI Web Site 1 Citations 10 References

Bibliographic Information

Other Title
  • 磁性材料　　Ｍｎ‐Ｚｎフェライトの磁気特性および微細構造に及ぼすＰｒ６Ｏ１１添加効果
  • Mn Zn フェライト ノ ジキ トクセイ オヨビ ビサイ コウゾウ ニ オヨボス Pr6O11 テンカ コウカ

Search this article

Abstract

This study describes the effect of Pr6O11 addition on the magnetic properties and the microstructures of the sintered Mn-Zn ferrite for high frequency power transformer uses. After calcination of mixed raw materials at 1000°C in nitrogen gas, the calcined powders were mixed with Pr6O11 in the concentration ranging from 0 to 0.8wt.% and then compacted. The compacted powders were sintered in air at the various temperatures of 1125-1225°C for 3 hours. When sintered at 1175°C, the coreloss at 50 mT and 200 kHz of sample added with 0.1 wt.% of Pr6O11 decreased to about a quarter of that of the sample without addition. Moreover, the initial permeability of the former sample increased by. about twice that of the latter sample. The fact suggests the formation of Fe2+ ions in the former sample caused by the substitution of Fe3+ ions by added Pr4+ ions.

Journal

Citations (1)*help

See more

References(10)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top