Change in Structure by Heat Treatment of SUS316L HS-PM Process Material.
-
- Matsuno Susumu
- KURIMOTO, LTD.
-
- Umekawa Sei
- Ritsumeikan University
-
- Ameyama Kei
- Department of Mechanical Engineering, Ritsumeikan University
Bibliographic Information
- Other Title
-
- SUS316L高ひずみ付加PMプロセス材の熱処理による組織変化
- SUS316L タカヒズミ フカ PM プロセスザイ ノ ネツ ショリ ニ ヨル ソシキ ヘンカ
Search this article
Description
The high strain powder metallurgy (HS-PM) process was applied to an SUS316L gas atomized powder by 360ks mechanical milling (MM) with a planetary ball mill under an Ar atmosphere. The MM powder was annealed at 1073 K, 1173 K, 1273 K. Each structure was investigated using XRD and TEM/EDS. It was confirmed that as-MM powder consisted of an ultra fine (α+γ) microduplex structure. It was supposed that the a phase was formed as the HS-PM process by increasing free energy of the austenitic phase. Fine grain structure with its grain size of 2.3μm composed of fine carbides and γ phase was obtained when MM powder was annealed at 1073 K for 3.6 ks. It was also confirmed that these fine carbides restrain the grain growth. But at 1173 K and 1273 K, the fine carbides were not seen, so that grain size increased drastically.
Journal
-
- Journal of the Japan Society of Powder and Powder Metallurgy
-
Journal of the Japan Society of Powder and Powder Metallurgy 49 (6), 479-485, 2002
Japan Society of Powder and Powder Metallurgy
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681286242688
-
- NII Article ID
- 10008833448
-
- NII Book ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL BIB ID
- 6190473
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed