Effects of Boron Content and Heat Treatment on Behavior of Complex Boride Forming in Ni - Cr - Mo - B Gas Atomized Powder with High Corrosion Resistant Matrix

DOI Web Site 3 Citations 12 References

Bibliographic Information

Other Title
  • 高耐食マトリックスを有するNi - Cr - Mo - B 系ガスアトマイズ粉末の複硼化物生成挙動 に及ぼすB 量および熱処理の影響
  • コウタイショク マトリックス オ ユウスル Ni-Cr-Mo-Bケイ ガスアトマイズ フンマツ ノ フクホウカブツ セイセイ キョドウ ニ オヨボス Bリョウ オヨビ ネツ ショリ ノ エイキョウ

Search this article

Description

The effects of B content and the heat treatment on the properties of gas atomized powders with Ni - 22 mass% Cr - X mass% Mo - Y mass% B compositions ((X, Y) = (23, 1.0), (26, 1.6), (30, 2.1), (33, 2.6)) were investigated. The powders were produced by gas atomization, followed by sieving under 150 µm in the particle size. Then the powders were heat treated at various temperatures to investigate the effects of the temperatures.<BR>As a result, the powders with less than 1.6 % B before the heat treatment consisted of only Ni - based supersaturated solid solution with B. On the other hand, in the powders with more than 2.1 % B before the heat treatment, not only Ni - based matrix but also coarse complex boride were observed. Tetragonal M3B2 type complex boride precipitated in all powders after the heat treatment at more than 1073 K. Furthermore, all examined powders after the heat treatment at 1473 K had almost the same matrix composition as Ni - 22 mass% Cr - 16 mass% Mo. Vickers hardness of these powders increased with increasing B content.

Journal

Citations (3)*help

See more

References(12)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top