Densification, Microstructure and Mechanical Properties of Reactive Hot-Pressed ZrB₂-ZrC-Zr Cermets
-
- GUO Shuqi
- Structural Non-oxide Ceramic Group, Research Center for Structural Materials, National Institute for Materials Science
書誌事項
- タイトル別名
-
- Densification, Microstructure and Mechanical Properties of Reactive Hot-Pressed ZrB<sub>2</sub>-ZrC-Zr Cermets
この論文をさがす
説明
<p>This study reviews densification behavior, microstructure and mechanical properties of the various composition ZrB2-ZrC0.6-Zr cermets prepared by reactive hot-pressing of Zr + B4C powder mixtures between 1673 K and 2173 K. During reactive sintering, densification consisted of two parts, one resulted from the volume contraction due to the conversion of Zr + B4C mixture into ZrB2 and ZrC0.6, other resulted from the shrinkage due to grain boundary diffusion and grain boundary migration that mostly contributed to the densification. Highly-dense ZrB2-ZrC0.6-Zr cermets were obtained for Zr + B4C mixtures at equal to or greater than 1673 K. The resulting ZrB2-ZrC0.6-Zr cermets consisted of platelet-like ZrB2 grains, equiaxed ZrC0.6 grains and intergranular Zr. The ZrB2 and ZrC0.6 grains were coarsened with increase of the excess Zr amount and/or sintering temperature. On the other hand, the flexural strength and fracture toughness of the cermets strongly depended on the excess Zr amount and/or sintering temperature. In addition, the crack propagation behavior of the cermets was associated with the excess Zr amount. The cracks directly propagated in the samples with less than 16 vol% Zr, however, the multiple cracking behavior was observed for the samples with equal to or greater than 16 vol% Zr.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 64 (8), 445-452, 2017
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681286859392
-
- NII論文ID
- 130006031927
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 028467928
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可