- Crystal Structure and Magnetic Properties of the Carbon-based Ferromagnet Prepared by Pyrolytic Method under High Magnetic Field
- キョウジバ チュウ ネツ ブンカイホウ ニ ヨッテ サクセイ シタ タンソケイ キョウジセイタイ ノ ケッショウ コウゾウ オヨビ ジキ トクセイ
この論文をさがす
抄録
We have prepared the carbon-based ferromagnets by pyrolytic method under high magnetic field and investigated their crystal structure and magnetic properties. The crystal structure was measured by the synchrotron X-ray diffraction experiment. The diffraction peak of a diamond was observed for the ferromagnetic samples. Thus, the carbon-based ferromagnet can be attributed to the ferromagnetic ordering of radical spins generated by defects in the diamond structure. And, the diffraction peak of a diamond of the ferromagnetic samples increased with the applied magnetic field in sample preparation. Therefore, the magnetic field may help to form a three dimensional ferromagnetic structure in the carbon-based ferromagnet. The highest magnetization was 3.0 emu/g at 300 K for the sample prepared under magnetic field at 6 T.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 58 (3), 176-180, 2011
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681287165312
-
- NII論文ID
- 10028125185
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3MXktFeqtLw%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 11053082
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可